Gd5Si1.75 Ge1.75 Sn0.5 was prepared by arc melting method. The crystal structure and magnetic properties were investigated by XRD and VSM, respectively. The magnetization of the Gd5Si1.75 Ge1.75 Sn0.5 alloy changes abruptly near its corresponding Curie temperature 269 K, possesses a typical first which means that the alloy order phase transition. The Gd5Si1.75Ge1.75 Sn0.5 adopts in Gd5Si2Ge2-type monoclinic structure at room temperature, the maximal magnetic entropy change at a magnetic field change of 1.8 T is as large as 16.7 J·kg^-1·K^-1, exceeding that of Gd about two times and is a little larger than that of Gd5Si2Ge2.
Gd5Si1.75 Ge1.75 Sn0.5 was prepared by arc melting method. The crystal structure and magnetic properties were investigated by XRD and VSM, respectively. The magnetization of the Gd5Si1.75 Ge1.75 Sn0.5 alloy changes abruptly near its corresponding Curie temperature 269 K, possesses a typical first which means that the alloy order phase transition. The Gd5Si1.75Ge1.75 Sn0.5 adopts in Gd5Si2Ge2-type monoclinic structure at room temperature, the maximal magnetic entropy change at a magnetic field change of 1.8 T is as large as 16.7 J·kg^-1·K^-1, exceeding that of Gd about two times and is a little larger than that of Gd5Si2Ge2.