摘要
A novel method was developed to fabricate monodispersed nanocomposite SiO2 sphere (200 ̄400 nm) containing homogeneously dispersed Ag nanoparticles (2 ̄6 nm). The morphology of inclusion was controlled through the N-[3-(Trimethoxysilyl)Propyl]ethylene diamine. TEM images showed that the silver nanoparticles were doped uniformly in silica spheres. UV-Vis showed that the doped silver nanoparticles have a plasmon resonance absorption band at 433 nm. Also SEM, EDX, XRD analyses were conducted to characterize thus-prepared sam- ples.
A novel method was developed to fabricate monodispersed nanocomposite SiO2 sphere (200-400 nm) containing homogeneously dispersed Ag nanoparticles (2-6 nm). The morphology of inclusion was controlled through the N-[3-(Trimethoxysilyl)Propyl]ethylene diamine. TEM images showed that the silver nanoparticles were doped uniformly in silica spheres. UV-Vis showed that the doped silver nanoparticles have a plasmon resonance absorption band at 433 nm. Also SEM, EDX, XRD analyses were conducted to characterize thus-prepared samples.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2006年第1期161-165,共5页
Chinese Journal of Inorganic Chemistry
基金
国家高技术研究发展计划(863计划)(No.2002AA302108)
国家自然科学基金(No.60372009
20301015)资助项目。
关键词
银
二氧化硅
掺杂
纳米复合颗粒
silver
silica
doping
nanoeomposite particles