摘要
通过对纯棉帆布阻燃整理工艺的选择、参数的优化,确定最佳工艺为:树脂70 g/L,阻燃剂400 g/L,磷酸20 g/L,纤维保护剂40 g/L,轧液率70%,180℃焙烘90 s。经测试,整理后织物的阻燃效果理想,手感较好,甲醛含量仅16 mg/kg,且耐水洗。
Flame resistance of cotton canvas on trial scale was optimized, the best conditions were obtained, such as resin 70 g/L, flame retardant 400 g/L, phosphoric acid 20 g/L, fiber protector 40 g/L, pick up 70 %, curing at 180 ℃ for 90 seconds. Bulk production is carried out according to results from trials, the finished fabric features good flame resistance, soft handle, ultra-low formaldehyde content （lower than 16 mg/kg）, as well as excellent washability.