钢板在冷弯时出现开裂,通过对开裂试样进行金相组织、冷弯断口形貌及能谱分析,结果表明,表面质量是导致冷弯性能不合格的原因之一,最后提出了相应的改进措施。
Plate create cracking when cold belting, the structure, cold bending fraction pttern and EXD of the plate are anaylzed.It is resulted the quality of surface are mainly reasons causing plate cold bending property, the improving ways were propose.
出处
《山西冶金》
CAS
2005年第3期44-45,共2页
Shanxi Metallurgy
关键词
冷弯性能
原因
分析
cold bending property, causes, analysis