研究了Ca对镁锰合金显微组织和腐蚀性能的影响。当镁锰合金中加入的Ca含量达到0.6%时,镁锰合金的晶粒显著细化,并且腐蚀速率下降为原来的11.8%。其原因主要是由于形成了Mg2Ca相,使镁锰合金的腐蚀电流密度降低,从而阻碍了镁锰合金的腐蚀。
The effect of calcium on microstructure and corrosion resistance of magnesium - manganese alloy was studied. Grain refinement can be greatly improved by adding 0.6% Ca element to magnesium - manganese alloy and the corrosion rate decreases to 11. 8%. This is mainly caused by the formation of Mg: Ca phase,which acts as an effective barrier against corrosion and makes the corrosion current density decreasing.