摘要
Vanadium alloys are considered as the promising first wall and structure materials of the future fusion reactors owing to their perfect low neutron-induced radioactivity and good high temperature performance. Helium retention and thermal desorption behaviors are key issues for the applications of vanadium alloys in fusion reactors since helium can be produced by helium discharge cleaning and neutron transmutation. A. van Veen groupt investigated helium trapping and thermal desorption mechanisms in vanadium alloys by using 1 keV helium ion irradiation to the fluence of 10^13～10^14He/cm^2, and the influenee of pre-annealing treatments on helium trapping. Two group of peaks were found at the thermal helium desorption spectrum. They thought one was due to helium-vacancyimpurity clusters and the other was corresponding to helium trapping into pre-existing traps, such as fine-size precipitates.