Dy^3＋-doped borate glasses （LBLB） with high effective visible fluorescence emission were synthesized. The absorption spectrum and fluorescence spectrum of this glass were measured and analyzed. By using J-O theory, the oscillator strengths for some absorption transitions were calculated according to the absorption spectra. The intensity parameters Ω1 （t = 2, 4, 6） of Dy^3＋ were determined by using a least-squares fitting approach, and the values are 4.04 × 10^-20, 1.30 × 10^-20 and 1.82 × 10^-20 cm, respectively. The root-mean-square deviation δrma was calculated. Under UV light excitation, Dy^3＋-doped borate glasses （LBLB） emit intense yellowish white lights. The excitation spectrum indicates that argon laser is the effective excitation source in Dy^3＋-doped LBLB glasses
Dy^3＋-doped borate glasses （LBLB） with high effective visible fluorescence emission were synthesized. The absorption spectrum and fluorescence spectrum of this glass were measured and analyzed. By using J-O theory, the oscillator strengths for some absorption transitions were calculated according to the absorption spectra. The intensity parameters Ω1 （t = 2, 4, 6） of Dy^3＋ were determined by using a least-squares fitting approach, and the values are 4.04 × 10^-20, 1.30 × 10^-20 and 1.82 × 10^-20 cm, respectively. The root-mean-square deviation δrma was calculated. Under UV light excitation, Dy^3＋-doped borate glasses （LBLB） emit intense yellowish white lights. The excitation spectrum indicates that argon laser is the effective excitation source in Dy^3＋-doped LBLB glasses