Preparation of Neodymium-Doped Yttrium Aluminum Garnet Transparent Ceramics by Homogeneous Precipitation Method 被引量:5

Preparation of Neodymium-Doped Yttrium Aluminum Garnet Transparent Ceramics by Homogeneous Precipitation Method
下载PDF
导出
摘要 substitutes tion, high loosely dis Neodymium doped-yttrium aluminum garnet (Nd : YAG) transparent polycrystalline ceramics already become of single crystals because they are provided with easy fabrication, low cost, large size, highly doped concentraheat conductivity, mass fabrication, multi-layers and multi-filnctions. The Nd:YAG precursor powders with persed , slightly agglomerated, super fine and YAG cubic crystal phase were synthesized at 1100 ℃ by the homogeneous precipitation method, using Nd2O3, Y2O3, Al(NO3)3·9H2O and urea as raw materials, (NH4)2SO4 as electrical stabilizer, TEOS as sintering additive. The Nd:YAG transparent ceramics were prepared after being vacuum sintered at 1700 ℃ for 5 h. The Nd:YAG ceramic materials were characterized by the TG-DTA, XRD, FT-IR, TEM, FEG-ESEM and FT-PL. The results show that the crystallization temperature of YAG is 850 ℃ and the intermediate crystal phase YAP forming during the heat treatment transforms to YAG cubic crystal phase at 1050 ℃. The lasing wavelength of (Nd0.01 Y0.99)3Al5O12 transparent ceramics is 1.065 μm and there exists a slight red-shift compared to the single crystal with the same chemical composition. The optical transmittance is 45 % in the visible light and 58 % in the near infrared light and the optical transmittance descends with the decreasing the wavelength. substitutes tion, high loosely dis Neodymium doped-yttrium aluminum garnet (Nd : YAG) transparent polycrystalline ceramics already become of single crystals because they are provided with easy fabrication, low cost, large size, highly doped concentraheat conductivity, mass fabrication, multi-layers and multi-filnctions. The Nd:YAG precursor powders with persed , slightly agglomerated, super fine and YAG cubic crystal phase were synthesized at 1100 ℃ by the homogeneous precipitation method, using Nd2O3, Y2O3, Al(NO3)3·9H2O and urea as raw materials, (NH4)2SO4 as electrical stabilizer, TEOS as sintering additive. The Nd:YAG transparent ceramics were prepared after being vacuum sintered at 1700 ℃ for 5 h. The Nd:YAG ceramic materials were characterized by the TG-DTA, XRD, FT-IR, TEM, FEG-ESEM and FT-PL. The results show that the crystallization temperature of YAG is 850 ℃ and the intermediate crystal phase YAP forming during the heat treatment transforms to YAG cubic crystal phase at 1050 ℃. The lasing wavelength of (Nd0.01 Y0.99)3Al5O12 transparent ceramics is 1.065 μm and there exists a slight red-shift compared to the single crystal with the same chemical composition. The optical transmittance is 45 % in the visible light and 58 % in the near infrared light and the optical transmittance descends with the decreasing the wavelength.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2005年第6期716-720,共5页 稀土学报(英文版)
基金 ProjectsupportedbytheChineseEducationMinistryExcellentTeacherFund(KB200226)
关键词 laser materials transparent ceramics neodymium-doped yttrium aluminum garnet (Nd:YAG) nano-sized powders low temperature combustion synthesis (LCS) rare earths laser materials transparent ceramics neodymium-doped yttrium aluminum garnet (Nd:YAG) nano-sized powders low temperature combustion synthesis (LCS) rare earths
  • 相关文献

参考文献3

二级参考文献37

  • 1Greskovich C, Chemoch J P. Improved polycrystalline ceramic lasers [J]. J. Appl. Phys., 1974, 45(10): 4495.
  • 2Greskovich C, Chemoch J P. Polycrystalline ceramic lasers[J]. J. Appl. Phys., 1973, 44(10): 4599.
  • 3Ikesue A, Kamata K, Yoshida K. Synthesis of transparent Nddoped HfO2-Y2O3 ceramics using HIP [J ]. J. Am. Ceram .Soc., 1996, 79(2): 359.
  • 4Greskovich C, Woods K N. Fabrication of transparent ThO2-doped Y2O3[J]. J. Am. Ceram. Soc., 1973, 52(5): 473.
  • 5Lefever R A, Matsho J. Transparent yttrium oxide ceramics[J]. Mater. Res. Bull., 1967, 2(9): 865.
  • 6Rhodes W H. Controlled transient solid second-phase sintering of tttria [J]. J. Am. Ceram. Soc., 1981, 64(1): 13.
  • 7Dutta S K, Gazza G E. Transparent Y2O3 by hot-pressing [J].Mater. Res. Bull., 1969, 4(11): 791.
  • 8Tsukuda Y, Muta A. Sin.ering of Y2O3 at high temperatures[J]. J. Ceram. Soc. Jpn., 1976, 84(12): 585.
  • 9Iga T, Izawa Y, High Purity. Fine α-alumina powder obtained by thermal decomposition of ammonium dawsonite [J ]. Transactions of the Materials Research Society of Japan [ M ]. 11 ( 1 -12), Edited by S.Somiya, M. Doyama, and Y.Agata. Materials Research Society of Japan, Tokyo, Japan. 1991.
  • 10Li Jiguang, Lee Jongheun, Mori T. Crystal phase and sinterability of wet-chemically derived YAG powders [J ]. J. Ceram.Soc. Japan., 2000, 108(5): 439.

共引文献31

同被引文献67

引证文献5

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部