We report the spectroscopic properties and thermal stability of Tm^3＋-doped Ga2O3-GeO2-Bi2O3-PbO（PbF2） glasses for 1.47-μm optical amplifications. Effects of PbF2 doping on the optical properties and thermal stability of Tm^3＋ -doped gallate-germanium-bismuth-lead glass are inestigated. The measured peak wavelength and full width at half-maximum of the fluorescence are 1465nm and - 120 nm, respectively： Siguificant enhancement of the 1.47-μm emission and the lifetime of a a^3H4 level with increasing PbF2 doping have been observed. The presence of GeO2 provides two potentials of increasing the thermal stability and shortening the ultraviolet cutoff band of host glasses.
We report the spectroscopic properties and thermal stability of Tm^3＋-doped Ga2O3-GeO2-Bi2O3-PbO（PbF2） glasses for 1.47-μm optical amplifications. Effects of PbF2 doping on the optical properties and thermal stability of Tm^3＋ -doped gallate-germanium-bismuth-lead glass are inestigated. The measured peak wavelength and full width at half-maximum of the fluorescence are 1465nm and - 120 nm, respectively： Siguificant enhancement of the 1.47-μm emission and the lifetime of a a^3H4 level with increasing PbF2 doping have been observed. The presence of GeO2 provides two potentials of increasing the thermal stability and shortening the ultraviolet cutoff band of host glasses.
基金
Supported by the National Natural Science Foundation of China under Grant No 50472053, the Department of Science and Tcchnology of Guangdong under Grant Nos 04020036 and 2004A10602002, and thc Department of Science and Technology of Guangzhou （2004Z2-D0131）.