摘要
利用扫描电镜对高强度螺栓断口进行了微观形貌观察与分析。结果表明,由于冶炼或浇注时,钢液内混入了耐火材料碎块,其杂质元素向晶界偏聚引起局域性的晶界脆化,从而导致螺栓在较低应力状态下发生断裂。
Based on the microanalyse, the fracture of the high strength stud bolt was analyzed by scanning electron microscope ( SEM ). It was observed that the tramp elements in the fire-proof material particles have separated out to the crystal boundary so that lead to local brittle crystal boundary, therefore the stud bolt was broken under small stress conditions.