摘要
为了更有利于血管内支架表面的药物涂层和内皮细胞的粘附,采用化学腐蚀后溶胶-凝胶法涂覆TiO_2薄膜和等离子体沉积的方法对血管内支架表面进行粗糙化表面改性。并对这两种改性方法的生物相容性进行评价,结果表明,改性后支架的粗糙度增大,提高了抗凝血性和亲水性,但抗腐蚀性的增加不显著。
This paper introduces the surface modification of NiTi alloy intravascular stents for roughness by chemical erosion and plasma deposition technology. The stent which had been granulated with chemical erosion was treated with TiO2 film prepared with Gel-sol. The study on the biocompatibility of the modified stent by the above two ways shows that the modified stent is rougher, and its anticoagulation and hydrophilicity are improved. However, the capability of erosion resistance is not enhanced significantly.