It was found that SrFeO3-xhas the oxygen breathing properties.The oxygen adsorption isotherms of SrFeO3-x were measured at temperature ranging from 300℃ to 700℃.The oxygen saturated adsorptivity increased with reducing temperature.And the activity of SrFeO3-x catalysing the oxidation of toluene was measured in air.Experimental results showed that the conversation of toluene on SrFeO3-x in air was improved with temperature rising up and space velocity slowing down.
It was found that SrFeO3-x,has the oxygen breathing properties. The oxygen adsorption isotherms of SrFeO3-x, were measured at temperature ranging from 300℃ to 700℃. The oxygen saturated adsorptivity increased with reducing temperature. And the activity of SrFeO3-x, catalysing the oxidation of toluene was measured in air. Experimental results showed that the conversation of toluene on SrFeO3-x, in air was improved with temperature rising up and space velocity slowing down.
出处
《化学研究与应用》
CAS
CSCD
北大核心
2006年第2期192-194,共3页
Chemical Research and Application
基金
河南省自然科学基金资助项目(311020700)