The effects of heat treatment on the properties of multi element wear-resistant low-alloy steel (MLAWS) which is used to make the liner of rolling mill torus were researched. The results show that when quenching temperature is lower than 900℃, the hardness increases with the increase of temperature, and when quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. As quenching temperature is lower than 920℃, the effect of quenching temperature on the impact toughness is not obvious. When quenching temperature is higher than 920℃ , impact toughness decreases with the increase of temperature. When tempering temperature is higher than 450 ℃ , the hardness begins to decrease obviously. After tempering at 350℃, the best wear resistance was obtained. According to the service condition of rolling mill torus liner, the MLAWS is quenched from 900-920 ℃ and tempered at 350-370℃.
The effects of heat treatment on the properties of multi element wear-resistant low-alloy steel (MLAWS) which is used to make the liner of rolling mill torus were researched. The results show that when quenching temperature is lower than 900℃, the hardness increases with the increase of temperature, and when quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. As quenching temperature is lower than 920℃, the effect of quenching temperature on the impact toughness is not obvious. When quenching temperature is higher than 920℃ , impact toughness decreases with the increase of temperature. When tempering temperature is higher than 450 ℃ , the hardness begins to decrease obviously. After tempering at 350℃, the best wear resistance was obtained. According to the service condition of rolling mill torus liner, the MLAWS is quenched from 900-920 ℃ and tempered at 350-370℃.
基金
ItemSponsored by Tackle-Key-Programof Science and Technology Committee of Henan Province (042426002 ,0535010700)
Henan Innovation Project for University Prominent Research Talents (2006KYCX022)