高强耐候钢相变组织变化规律研究 被引量:11

Transformation Microstructure Evolution Rules of High Strength Weathering Steel
下载PDF
导出
摘要 进行了400MPa级高强耐候钢的成分设计和试验室冶炼,通过热模拟试验,分析了不同工艺条件下奥氏体晶粒的变化规律;并进一步测定了试制钢的动态、静态CCT曲线,对其相变规律进行了初步研究。结果表明:动态连续冷却转变温度略高于静态转变,动态连续转变γ+α两相区的温度区间在100℃以上,静态连续冷却转变两相区的温度区间在70~90℃之间;冷却转变的显微组织为大量铁素体和部分珠光体。 Composition design and smelting of 400 MPa high strength weathering steel were carried out in laboratory. On the basis of thermal simulation experiment of slab, evolution rules of austenitic microstructure under different process conditions were analyzed. Static and dynamic CCT curves of the experimental steel were tested further, and the phase transformation rules were investigated. The transformation temperature of dynamic CCT was higher than that of static CCT, and temperature range of γ+α critical zone of dynamic CCT was over 100 ℃ while that of static CCT was in the range of 70- 90℃ : the microstructure consisted of a amount of ferrite and partial pearlite.
出处 《机械工程材料》 CAS CSCD 北大核心 2006年第1期12-15,共4页 Materials For Mechanical Engineering
关键词 高强耐候钢 相变 CCT曲线 high strength weathering steel transformation CCT curve
  • 相关文献

参考文献6

二级参考文献14

  • 1Delu Liu, Xangdong Huo, Yuanli Wang, Jie Fu, Yongin Kang, Nanjing Chen 1 ) Materials Science and Engineering School, University of Science and Technology Beijing, Bejing 100083, China 2) Metallurgy School, University of Science and Technology Beijing, Bei.Oxide and Sulfide Dispersive Precipitation in Ultra-low Carbon Steels[J].Journal of University of Science and Technology Beijing,2001,8(4):314-315. 被引量:10
  • 2Bepan M A and Whiteman J A. Tne Effect of Nitrogen on the Precipitation Behavior of Nb ( C, N ) in Continuously-Cooled Low-Carbon Structural Steel. Journal of Materials Processing Technology, 1996(56) : 839.
  • 3Yuji Kirtrara and Setsuo Takaki. Phase Transformation Mechanism of Fe-Cu Alloys. ISIJ International, 1997,37 (3) : 290.
  • 4Okaguchi S, Hashimoto T and Ohtani H. Effect of Nb, V and Ti on Transformation Behavior of HSLA Steel in Accelerated Cooling. Thermec Iron and Steel Institute of Japan, 1988:330.
  • 5Zackay V F, Parker E R, Fahr D. The enhancement of ductility on high-strength steels[J]. Trans ASM,1967,60:252-259.
  • 6Sakuma Y Matsumura O, Takechi H. Mechanical properties and retained austenite in intercritically heat-treated bainite-transformed steel and their variation with Si and Mn additions[J]. Metall Trans,1991,22A:489-498.
  • 7Sugimoto K I, Misu M, Kobayashi M. Effects of second phase morphology on retained austenite morphology and tensile properties in a TEIP-aided dual-phase steel sheet[J]. ISIJ Int,1993,33:775-782.
  • 8Jacques P J, Ladriere J, Delannay F. On the influence of interactions between phase on the mechanical stability of retained austenite in transformation-indeced plasticity multiphase steels[J]. Metall Trans,2001,32A:2759-2768.
  • 9Meyer M D, Vanderschueren D, Cooman B C D, et al. The influence of the substitution of Si by Al on the properties of cold rolled C-Mn-Si TRIP steels[J]. ISIJ Int,1999,39:813-822.
  • 10Hanzaki A Z, Yue S. Ferrite formation characteristics in Si-Mn TRIP steels[J]. ISIJ Int,1997,37:583-589.

共引文献44

同被引文献77

引证文献11

二级引证文献29

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部