利用真空浸渍法制得碳纤维增强环氧复合材料,研究了阳极氧化处理前后碳纤维表面状态的变化及表面处理对复合材料力学性能的影响。结果表明:适当的阳极氧化处理使复合材料的弯曲和剪切性能有很大改善,但冲击性能有所降低。
An epoxy-based composite reinforced with carbon fibers （C/EP） was prepared by vacuum impregnation process. The specific surface area and tensile fracture load of carbon fibers were determined after anodic oxidation treatment, and the effects of fibers surface treatment on mechanical properties of C/EP composites were also discussed. The anodic oxidation resulted in the reduction of fiber＇s tensile strength, the larger the current density and the longer the oxidation time, the more the loss. The specific surface area of carbon fibers increased with the oxidation time when the current density was 2 A/m^2 and initially increased then decreases at 1 A/m^2. The flexural and shear properties of the C/EP composites with properly oxidized fibers were greatly improved, while the impact strength failed to some extent. It＇s believed that the interface adhesion of the C/EP composite could be enhanced by the anodic oxidation treatment of carbon fibers, but the oxidation time should not exceed 2 minute in order to obtain a better general mechanical performance.
出处
《机械工程材料》
CAS
CSCD
北大核心
2006年第1期53-55,共3页
Materials For Mechanical Engineering