在哈克流变仪中将炭黑(CB)与聚苯乙烯(PS)、尼龙6(PA6)共混,研究了CB在PS/PA6/CB共混体系中的分散情况及CB含量和PS与PA6的质量比对PS/PA6/CB共混体系导电性能、微观形态的影响。结果表明,CB在PS/PA6/CB共混体系中只分散在PA6中;PS/PA6/CB共混体系的导电性能随着CB含量的增加而增强,CB的体积分数在20%-40%时,PS/PA6/CB共混体系的电导率增幅明显;PS、PA6两相的微观尺寸随CB含量增加而变小;PS/PA6/CB共混体系中PS与PA6质量比约为80/20时,PS/PA6/CB共混体系的导电性能最好。
Polystyrene ( PS), nylon 6 (PA6) and carbon black (CB) are blended in Haake blender. The dispersion of CB in PS/PA6/CB blend and the effects of content of CB and mass ratio of PS to PA6 on the conductivity and morphology of PS/PA6/CB blend are studied. The results show that CB is dispersed in PA6 phase in PS/PA6/CB blend; the conductivity of PS/PA6/CB blend gets better with CB content increasing, especially when the volume fraction of CB is 20% -40% ; the microcosmic sizes of PS and PA6 phases turn small when CB content increases; the conductivity of PS/PA6/CB blend is the best when the mass ratio of PS to PA6 is about 80/20.
出处
《工程塑料应用》
CAS
CSCD
北大核心
2006年第2期7-10,共4页
Engineering Plastics Application
基金
国家自然科学基金资助项目(20276060)
关键词
炭黑
聚苯乙烯
尼龙6
导电性能
carbon black, polystyrene, nylon 6, conductivity