The nanocrystalline Bi2O3-Y2O3 solid electrolyte material was synthesized by pressureless reactive sintering process with Bi2O3 and Y2O3 nano mixed powder as raw materials, which was prepared by a chemical coprecipitation process. The study on the behavior of nano δ-Bi2O3 formation and its grain growth showed that the solid solution reaction of Y2O3 and δ-Bi2O3 to form δ-Bi2O3 occurs mainly in the initial stage of sintering process, and nano δ-Bi2O3 crystal grains grow approximately following the rule of paracurve ((D-D0)^2=K.t) during sintering process. After sintered at 600℃ for 2 h, the samples could reach above 96% in relative density and have dense microstructure with few remaining pores, the δ-Bi2O3 grains are less than 100 nm in size.
The nanocrystalline Bi2O3-Y2O3 solid electrolyte material was synthesized by pressureless reactive sintering process with Bi2O3 and Y2O3 nano mixed powder as raw materials, which was prepared by a chemical coprecipitation process. The study on the behavior of nano δ-Bi2O3 formation and its grain growth showed that the solid solution reaction of Y2O3 and δ-Bi2O3 to form δ-Bi2O3 occurs mainly in the initial stage of sintering process, and nano δ-Bi2O3 crystal grains grow approximately following the rule of paracurve ((D-D0)^2=K.t) during sintering process. After sintered at 600℃ for 2 h, the samples could reach above 96% in relative density and have dense microstructure with few remaining pores, the δ-Bi2O3 grains are less than 100 nm in size.
基金
financially supported by the National Nature Science Foundation of China (No.20101006)
the Nano Technology Special Foundation of Shanghai Science and Technology Committee (No.O452nm073)