摘要
Polyacrylonitrile-block-poly（methyl acrylate）（P（AN-b-MA）） was synthesized by reversible addition-fragmentation chain transfer （RAFT） polymerization employing macro-RAFT agent （PAN-RAFT） as the chain transfer agent and azobis（isobutyronitrile） （AIBN） as the initiator. A linear relationship between ln（[M]0/[M]1） and reaction time was observed. The molecular structure of P（AN-b-MA） was characterized by ^1H-NMR, element analysis, FTIR and SEC. The molecular weight distribution （MWD） was less than 1.40, the Mn could be controled from 0.733 to 4.834×10^4, and the molar content of MA in P（AN-b-MA） were from 15.6 to 75.0 percentage, respectively.
Polyacrylonitrile-block-poly（methyl acrylate）（P（AN-b-MA）） was synthesized by reversible addition-fragmentation chain transfer （RAFT） polymerization employing macro-RAFT agent （PAN-RAFT） as the chain transfer agent and azobis（isobutyronitrile） （AIBN） as the initiator. A linear relationship between ln（[M]0/[M]1） and reaction time was observed. The molecular structure of P（AN-b-MA） was characterized by ^1H-NMR, element analysis, FTIR and SEC. The molecular weight distribution （MWD） was less than 1.40, the Mn could be controled from 0.733 to 4.834×10^4, and the molar content of MA in P（AN-b-MA） were from 15.6 to 75.0 percentage, respectively.