A new type of large-displacement actuator called reduced and internally biased oxide wafer （RAINBOW） is fabricated by chemical reduction of Pb（Sn, Zr, Ti）O3（PSZT） antiferroelectric ceramics and its properties are investigated. It is found that PSZT is easily reduced and the optimal conditions for producing RAINBOW samples are determined to be 870 ℃ for 2-3 h. The antiferroelectrics-ferroelectrics phase transitions occur at lower field strength in RAINBOW actuators compared with normal PSZT actuators. Large axial displacements are also obtained from the RAINBOW actuator by application of electric fields exceeding the phase switching level. However, the field-induced displacement of the RAINBOW actuator is dependent on the manner of applying load on the samples.
A new type of large-displacement actuator called reduced and internally biased oxide wafer （RAINBOW） is fabricated by chemical reduction of Pb（Sn, Zr, Ti）O3（PSZT） antiferroelectric ceramics and its properties are investigated. It is found that PSZT is easily reduced and the optimal conditions for producing RAINBOW samples are determined to be 870 ℃ for 2-3 h. The antiferroelectrics-ferroelectrics phase transitions occur at lower field strength in RAINBOW actuators compared with normal PSZT actuators. Large axial displacements are also obtained from the RAINBOW actuator by application of electric fields exceeding the phase switching level. However, the field-induced displacement of the RAINBOW actuator is dependent on the manner of applying load on the samples.
基金
This project is supported by National Natural Science Foundation of China (No.50135030)Aeronautical Science Foundation of China(No.04G52042)Pre-research fund of Weapons & Equipments of China(No.51412010505HK0208).