A rapid analysis method of determining content of eight compounds of open-hearth furnace slag was developed using X-ray fluorescence spectrometry and pressed powder briquettes. Matrix effect was corrected using theoretical alpha coefficient. Grains-size effect was eliminated by optimized sample preparation technique parameters. Mineral effect was corrected with standard curve of specially made standard samples. The analysis results of TiO2, TFe, SiO2, MgO, Al2O3, CaO, MnO and P2O5 in slag samples showed that both precision and accuracy are comparable with that of chemical method.
A rapid analysis method of determining content of eight compounds of open-hearth furnace slag was developed using X-ray fluorescence spectrometry and pressed powder briquettes. Matrix effect was corrected using theoretical alpha coefficient. Grains-size effect was eliminated by optimized sample preparation technique parameters. Mineral effect was corrected with standard curve of specially made standard samples. The analysis results of TiO2, TFe, SiO2, MgO, Al2O3, CaO, MnO and P2O5 in slag samples showed that both precision and accuracy are comparable with that of chemical method.