目的:测试Dyract的理化性能。方法:用拉力机、显微硬度机测试。结果:固化深度光照40s达8mm;径向拉伸强度42.4±7.16MPa,性能相似于复合树脂Durafil和Pekalux;表面硬度为HV31.9±3.84,也近似Durafil和Pekalux;剪切粘结强度为8.54±2.05MPa,温度交替后为8.41±2.50MPa。
Aim:The physicochemical characteristics of Dyract were tested. Methods:Tension test machine and microhardness tester were used. Results: The curing depth by light for 40s was 8mm. Diametral tensile strength of Dyract was 42.4±7.16 MPa, similar to that of Durafill 38.09±7.83, and Pekalux 31.11±5.55. The surface hardness of Dyract was 31.9±3.84(HV), similar to that of Durafill 27.52±1.23 and Pekalux 21.68±1.98. The shear bond strength of Dyract was 8.54±2.05MPa, and 8.41±2.50MPa after thermocycling. Conclusionns: Dyract is a new type filling material for anterior teeth and deciduous teeth.