A new metal-organic coordination polymer [Zn（ipt）（im）2]2n·3nH2O 1 has been obtained by using hydrothermal synthesis and characterized by elemental analysis, IR, TG, fluorescence spectrum and single-crystal X-ray diffraction. The complex crystallizes in monoclinic, space group P2（1/n） with a = 10.653（3）, b = 17.891（6）, c = 10.743（4）A^°,β= 117.093（5）°, V= 1822.9（10） A^°3, Mr= 413.65, Dc = 1.507 g/cm^3,/t（MoKa） = 1.390 mm^-1, F（000） = 840, Z = 4, the final R = 0.0444 and wR = 0.1066 for 2434 observed reflections （I〉 2σ（I））. Furthermore, compound 1 shows blue photoluminescent property at room temperature.
A new metal-organic coordination polymer [Zn（ipt）（im）2]2n·3nH2O 1 has been obtained by using hydrothermal synthesis and characterized by elemental analysis, IR, TG, fluorescence spectrum and single-crystal X-ray diffraction. The complex crystallizes in monoclinic, space group P2（1/n） with a = 10.653（3）, b = 17.891（6）, c = 10.743（4）A^°,β= 117.093（5）°, V= 1822.9（10） A^°3, Mr= 413.65, Dc = 1.507 g/cm^3,/t（MoKa） = 1.390 mm^-1, F（000） = 840, Z = 4, the final R = 0.0444 and wR = 0.1066 for 2434 observed reflections （I〉 2σ（I））. Furthermore, compound 1 shows blue photoluminescent property at room temperature.
基金
The project was supported by the Education Office of Jilin Province (No. 0047)