摘要
为了进一步提高铁镍热磁合金的性能,系统研究了Mo元素对铁镍热磁材料的磁滞回线、Ms-T曲线和热磁性能的影响规律。结果表明:随Mo含量的增加,Fe65.84-xNi34.16Mox(x=2,3,4,5)合金的磁滞回线逐渐变得扁平,饱和磁感应强度值(Bm)、饱和磁化强度值(Ma)和居里温度(Tc)单调下降,温度系数△B/△C(0~100℃)值呈先升高后降低的趋势,并在Mo含量为4at%附近出现最高值5.86mT/℃。
The effects of the Mo content in nickel -iron thermomagnetic alloy on the hysteresis loop, Ms-T curve and thermomagnetic property were investigated. The results show that with increasing content of Mo in Fe65.84-xNi34.16Mox ( x = 2,3,4,5 ) alloy, the hysteresis loop becomes flat, Bm ( M, ) and Tc decrease, but △B/△C(0~100℃) decreases after an increase and there's a peak of 5.86mT/℃ when the content of Mo is 4at%.