摘要
Weldability test was carried out on the newly developed fine grain, low sulphur, high strength and high toughness pipeline steel of X80 and its matching SAW wire. Test of maximum hardness in welding heat-affected zone and test of Y groove cracking show that X80 steel features low hardenability and good cracking resistance. The submerged arc welding joint made with the newly developed low carbon and multi-alloyed SAW wire of WGX2 exhibits a little higher strength than the base metal, qualified bending performance, under maximum limitation hardness and good impact toughness, which can completely meet the technical requirement of X80 steel. Despite somewhat coarsening the grain size in welding heat-affected zone is still much finer than that of traditional steels, and the microstructure in weld metal is almost full acicular ferrite. The results show that X80 steel and WGX2 wire are of great weldability.
Weldability test was carried out on the newly developed fine grain, low sulphur, high strength and high toughness pipeline steel of X80 and its matching SAW wire. Test of maximum hardness in welding heat-affected zone and test of Y groove cracking show that X80 steel features low hardenability and good cracking resistance. The submerged arc welding joint made with the newly developed low carbon and multi-alloyed SAW wire of WGX2 exhibits a little higher strength than the base metal, qualified bending performance, under maximum limitation hardness and good impact toughness, which can completely meet the technical requirement of X80 steel. Despite somewhat coarsening the grain size in welding heat-affected zone is still much finer than that of traditional steels, and the microstructure in weld metal is almost full acicular ferrite. The results show that X80 steel and WGX2 wire are of great weldability.