摘要
采用X射线衍射法研究了RuO2-SnO2混合金属氧化物电极的相结合和晶格参数。结果表明:RuO2和SnO2形成了具有金红石型结构的固溶体,但与RuO2-TiO2电极比较,晶粒较为细小,因此涂层较致密,采用循环伏安法研究了电极的活性表面(q)结果显示,RuO2-SnO2电极具有较小的电极外表面和较大的是极内表面,上述结果有助于说明RuO2-SnO2电极稳定性提高的原因。
The phase structure and lattice constants of RuO_2-SnO_2 mixed metal oxides electrode was investigated by XRD.It was found that mixed oxides system formed a solid solution of RuO_2- SnO_2 with a rutile- type structure,but it had a smaller crystalline size and more compact than the RuO_2-TiO_2 system. Cyclic voltammetry provided information about electrochemically active surface area(q).The results indicated that for RuO- SnO_2 (associated with the external surface)was less and (associated with the internal surtface) was bigger than that of RuO_2-TiO_2. The enhancement of stability for Ru-Sn can be attributed to more compact oxide layer and the formation of a stable Ru-Sn compound.