激光焊接块体非晶合金Zr45Cu48A17 被引量:1

Laser welding of bulk metallic glass Zr45Cu48Al7
下载PDF
导出
摘要 采用传统激光焊接技术连接块体非晶合金Zr45Cu48Al7,试验结果显示:焊接速率为2m/min时,熔化区主要生成τ5(Zr38Cu36Al26)相,热影响区主要生成ZrCu相,含有少量τ5相;焊接速率为4m/min时,熔化区保持了非晶特性,热影响区有晶粒生成;当焊接速率8m/min时,热影响区和熔化区均保持非晶特性。 Using a conventional laser welding method,we have welded two pieces of bulk metallic glasses of Zr45Cu48A17 without crystallization.The results indicates that the majority of the compounds in molten zone were produced to be τ5(Zr38Cu36A126),those in the HAZ were ZrCu with small amount of τ5 when the welding speed was 2 m/min,and the compounds existed in HAZ and the molten zone kept amorphous ,while the welding speed was 4 m/min ,and the formation of any crystalline phases was not detected at the interface, When the welding speed was 8 m/min.
出处 《电焊机》 2006年第4期60-62,共3页 Electric Welding Machine
基金 江西省材料科学和工程研究中心资助项目(ZX200401004)
关键词 块体非晶合金 激光焊接 热影响区 熔化区 bulk metallic glass laser welding heat-affected zone molten zone
  • 相关文献

参考文献10

  • 1Inoue A.Stabilization of metallic supercooled liquid and bulk amorphous alloys[J].Acta mater,2000(48):279-285.
  • 2Inoue A, Nakamura T, Nishiyama N,et al.Mg-Cu-Y Bulk Amorphous Alloys with High Tensile Strength Produced bya High-pressure Die Casting Method[J].Mater. Trans. JIM.,1992, (33) : 937-945.
  • 3Inoue A.High Strength Bulk Amorphous Alloys with Low Critical Cooling Rates[J].Mater. Trans. JIM, 1995,(36):866-875.
  • 4Bush R, Liu W,Johnson W L.Thermodynamics and Kinetics of the Mg65Cu25Y10 Bulk Metallic Glass Forming Liquid[J].Jpn J. Appl. Phys, 1998, (83) :4134-4141.
  • 5Men H, Yang M C ,Jian X U.Glass-forming Ability of Mg-Cu-Co-Y Alloy[J].Mater. Sci. Forum., 2002(386-388):39-46.
  • 6Bartusch B,Schurack F, Eckert J.High Strengh Magnesiumbased Glass Matrix Composites[J].Mater. Trans. JIM. ,2002(43):1979-1984.
  • 7Inoue A.Bulk Amorphous Alloys,Preparation and Fundamental Characteristics[M].NH :Trans Tech Publications, 1998.
  • 8Kawamura Y, Kagao. S, Ohno. Y.Electron Beam Welding of Zr-Based Bulk Metallic Glass to Crystalline Zr Metal[J].Mater Trans, 2001 , 42(12) : 2649-2651.
  • 9Kawamura Y, Ohno. Y.Successful Electron-beam Welding of Bulk Metallic Glass[J].Mater Trans, 2001,42(11): 2476-2478.
  • 10Yokobuyuki. Y, Abe. N, Fukaura. K,et al.Electron Beam Welding of Zr50Cu30Ni 10AI10 Bulk Glassy Alloys[J].Mater Trans, 2002,43(10) : 2509-2515.

同被引文献10

  • 1lnoue A.Stabilization of metallic supercooled liquid and bulk amorphous alloys[J].Acta Mater., 2000(48) : 279-285.
  • 2Peker A,Johnson W L,Schafer R.Amorphous metal/diamond composite material[P].US Patent, 1996(5): 567,532.
  • 3Inoue A,Zhang T, Nishiyama N.Preparation of 16 mm diame- ter rod of amorphous Zr65AlT7.5Nil0CulT175 alloy[J].Mater. Trans. JIM, 1993,34(12): 1234-1237.
  • 4Xia C,Xing L, Long W Y ,et a/.[不详].Jounml of Alloys and Compounds, 2009(484) : 698.
  • 5Kawamura Y,Ohno Y.Successful electron beam welding of bulk metallic glas[J].Mater Trans,2001,42(11): 2476-2478.
  • 6Yokobuyuki Y, Abe N, Fukaura K,et a/.Electron beam welding of Zr50Cu30Nil0Al10 bulk glassy alloys[J].Mater Trans, 2002,43(10) : 2509-2515.
  • 7Wang H S,Chen H G,Jang J S C,et td.Combination of a Nd:YAG laser and a liquid cooing device to (Zr53Cu30NigAjs) Si0.5 bulk metaic gass wehting[J].Materials Science and Engineering A, 2010(528) : 338-341.
  • 8Tam R C Y,Shek C H.Relaxation and c'rystallization of Zr4taTilaaCul125Ni10Be225[J].Materials Science and Engineering A, 2004,364(1,2) : 198-201.
  • 9Huei-Sen Wang, Hou-Guang Chen,Jason Shian-Ching Jang. Microstructure evolution in Nd:YAG laser-welded (Zr53Cu30- NigAis)Si0.5 bulk metallic glass alloy[J].Journal of Alloys and Compounds, 2010(495) : 224-228.
  • 10Lu K.The temperature versus time transformation (T-T-T) diagram for a transition from the amorphous to the nanot'rys- talline state[J].Acta. Metallurgica et Materialia, 1994(42): 2303-2312.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部