GaAs nanocrystals were prepared via a simple mechanical ball milling technique. The prepared GaAs nanocrystals have high purity and could form colloidal ethanol suspension without any surfactant additives. The colloidal GaAs nanocrystal suspension displayed excellent two-photon absorption property over the visible and near-infrared region from 490 nm to 1064 nm, which enables it to become a promising broadband optical limiting material.
GaAs nanocrystals were prepared via a simple mechanical ball milling technique. The prepared GaAs nanocrystals have high purity and could form colloidal ethanol suspension without any surfactant additives. The colloidal GaAs nanocrystal suspension displayed excellent two-photon absorption property over the visible and near-infrared region from 490 nm to 1064 nm, which enables it to become a promising broadband optical limiting material.
基金
The work was financially supported by the National Natural Science Foundation of China (Nos. 10104003, 10204003, 90206003, and 90101027) and the National Key Basic Research Special Foundation of China (No.TG1999075207).