Single crystalline ZnSe nanowires with both zincblende and wurtzite structures have been synthesized via a chemical vapour deposition method under different growth conditions. The nanowires are usually 50-80nm in diameter, and several tens of microns in length. Room-temperature photoluminescence spectra from zincblende and wurtzite ZnSe nanowires show a broad luminescence band peaked at around 2. 71 e V and a deep level emission band peaked at around 2.00 eV, respectively. Effects of post-growth annealing on the photoluminescence of these nanowires have been investigated. Strong room-temperature band-edge emission could be obtained from the annealed zincblende ZnSe nanowires.
Single crystalline ZnSe nanowires with both zincblende and wurtzite structures have been synthesized via a chemical vapour deposition method under different growth conditions. The nanowires are usually 50-80nm in diameter, and several tens of microns in length. Room-temperature photoluminescence spectra from zincblende and wurtzite ZnSe nanowires show a broad luminescence band peaked at around 2. 71 e V and a deep level emission band peaked at around 2.00 eV, respectively. Effects of post-growth annealing on the photoluminescence of these nanowires have been investigated. Strong room-temperature band-edge emission could be obtained from the annealed zincblende ZnSe nanowires.
基金
Supported by the National Natural Science Foundation of China under Grant Nos 10374004, 90201037, and 50172001, the State Key Lab on Integrated 0ptoelectronics, and the National Center for Nanoscience and Technology, China.