摘要
通过测量样品的磁化强度-温度曲线、电阻率-温度曲线及磁电阻-温度曲线.研究了 Dy 掺杂(0.00≤x≤0.30)对 La_(0.7-x)Dy_xSr_(0.3)MnO_3 体系磁电性质的影响.实验发现,随 Dy 掺杂量的增加,体系磁结构从长程铁磁有序向自旋团簇玻璃态、反铁磁状态转变；x=0.20、0.30时的低温磁行为发生异常,电行为存在低温电阻率极小值现象.这些奇特现象不仅来源于掺杂引起的晶格效应,也来源于掺杂引起的额外磁性耦合.
By measuring M-T curves, ρ-T curves and MR-T curves of the samples under different temperatures, the influence of Dy doping （0.00 ≤ x ≤0.30） on the magnetic and electric properties of La0.7-xDyxSr0.3MnO3 has been studied. The experimental results show that, with the increase of the Dy content, the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order. For the samples with x=0.20 and 0.30, their magnetic behaviors are abnormal at low temperature, and their resistivities at low temperature have a minimum value. These peculiar phenomena not only come from the lattice effect induced by doping, but also from extra magnetic coupling induced by doping.
基金
This work was supported by the National Nature Science Foundation of China （No. 19934003）
the State Key Project of Fundamental Research of China （No.001CB610604）
the Item of Nature Science Research of Anhui （No. 2001kj244）.
关键词
锰氧化物
低温电阻率反常
晶格效应
额外磁性耦合
Manganite, Abnormality of resistivity at low temperature, Lattice effect, Extra magnetic coupling