Weldability and Microstructure of Nickel-Silicon Based Alloys 被引量:1

Weldability and Microstructure of Nickel-Silicon Based Alloys
下载PDF
导出
摘要 The NiSix based alloy typically has poor weldability due to its lower ductility. A limited amount of work has been performed on the weldability of NiSix based alloys. Therefore, the effect of heat treatment and welding parameters on weldability of the alloys, and the relationship between the weldability and microstructure were studied. The results show that the as-cast Ni-Si-Nb-B alloy (Ni 76. 5%, Si 20%, Nb 3%, and B 0. 5%) could be successfully welded after preheating at 600 ℃. The welding procedure should be performed on the alloys before any heat treatment and a preheating at 600 ℃ should be used. The fusion zone is harder than the matrix due to a large amount of 7 phase and a finer microstructure. The cracks are predominantly intergranular in heat affected zone and associated with the needle-like ), phase. The heat treatment before welding increases the tendency of cracking in the fusion zone. The NiSix based alloy typically has poor weldability due to its lower ductility. A limited amount of work has been performed on the weldability of NiSix based alloys. Therefore, the effect of heat treatment and welding parameters on weldability of the alloys, and the relationship between the weldability and microstructure were studied. The results show that the as-cast Ni-Si-Nb-B alloy (Ni 76. 5%, Si 20%, Nb 3%, and B 0. 5%) could be successfully welded after preheating at 600 ℃. The welding procedure should be performed on the alloys before any heat treatment and a preheating at 600 ℃ should be used. The fusion zone is harder than the matrix due to a large amount of 7 phase and a finer microstructure. The cracks are predominantly intergranular in heat affected zone and associated with the needle-like ), phase. The heat treatment before welding increases the tendency of cracking in the fusion zone.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2006年第3期61-67,共7页
基金 Item Sponsored by State Key Lab of Mechanical Transmissions,Chongqing University
关键词 WELDABILITY Ni3Si based alloy heat treatment heat affected zone weldability Ni3Si based alloy heat treatment heat affected zone
  • 相关文献

参考文献14

  • 1Y. Zhou,S. J. Dong,K. J. Ely.Weldability of thin sheet metals by small-scale resistance spot welding using high-frequency inverter and capacitor-discharge power supplies[J].Journal of Electronic Materials.2001(8)
  • 2E. M. Lehockey,G. Palumbo,P. Lin.Improving the weldability and service performance of nickel-and iron-based superalloys by grain boundary engineering[J].Metallurgical and Materials Transactions A.1998(12)
  • 3C. L. White,D. F. Stein.Sulfur segregation to grain boundaries in Ni3Al and Ni3(AI,Ti) alloys[J].Metallurgical Transactions A.1978(1)
  • 4R. Moskovic.Phase transformations occurring in Ni-rich NiAl during quenching[J].Journal of Materials Science.1977(3)
  • 5Takasugi T,Nagashi ma M,Izumi O.Strengthening and Duc- tilization of Ni3Si by the Addition of Ti Elements[].Acta Metallurgica.1990
  • 6LI UJing-chuan,White C L,Horton J A.Effect of Boron on Grain-Boundaries in Nickel-Aluminum(Ni3Al)[].Acta Met- all.1985
  • 7Anthony I Taub,Briant C L.Ductility in Boron-Doped , Nick- el-Base Ll2 Alloys Processed by Rapid Solidification[].Scrip- ta Metall.1986
  • 8Sakata Hirosawa,Sato T,Kamio A,et al.Classification of the Role of Microalloying Elements in Phase Decomposition of Al Based Alloys[].Acta Materialia.2000
  • 9Stan A David,Wartan AJemian,LI UJing-chuan.Effect of the Different Crystal Structures of Boron Nitride on Its High- Temperature Stability in Oxygen[].Welding Journal.1985
  • 10Takasugi T,Shindo D,Izumi O,et al.Metallographic and Structural Observations in the Pseudo-Binary Section Ni3Si- Ni3Ti of the Ni-Si-Ti System[].Acta Metallurgica.1990

同被引文献13

  • 1郎永胜.WH80钢板的焊接性试验研究[J].宽厚板,2004,10(6):5-9. 被引量:2
  • 2黄治军,胡伦骥,缪凯,张小枫,陈浮.Weldability and SAW welding wire of X80 pipeline steel[J].China Welding,2006,15(1):74-80. 被引量:5
  • 3CHAI Feng,YANG Cai-fu,SU Hang,ZHANG Yong-quan,XU Zhou.Evaluation of Cracking Resistance of Copper-Bearing Age Hardening Steel Weldment[J].Journal of Iron and Steel Research International,2007,14(3):56-62. 被引量:1
  • 4CZYRYCA E J.Advances in high strength steel technology for naval hull construction[J].Key Eng.Mater.,1993,84-85:491-520.
  • 5SPANOS G,FONDA R W,VANDERMEER R A,et al.Microstructural changes in HSLA-100 steel thermally cycled to simulate the heat-affected zone during welding[J].Metall.and Mater.Trans.,1995,26A:3277-3293.
  • 6LUNDIN C D,MENON R,LAWSON J M.HAZ transformation and toughness in A710 grade a class 3 precipitation-strengthened steel[J].Welding Journal,1989,68(12):467s-472s.
  • 7KUMAR S.Weldability and microstructural aspects of shielded metal arc welded HSLA-100 steel plates[J].ISIJ International,2002,32(9):290-298.
  • 8ZHANG Wenyue.Welding metallurgy[M].Beijing:China Machine Press,2004.
  • 9YUKIO,TOMITA,TOSHIAK,et al.Development of 590 MPa class high tensile strength steel with superior HAZ toughness by copper precipitation[J].ISIJ International,1994,34(10):836-842.
  • 10LIU Wenyan,WANG Lai,LIU Jibin,et al.Microstructures and properties in simulated heat-affected zones of 685 MPa grade copper-bearing steel[J].Journal of Iron and Steel Research,Suppl.1,2007,14:220-227.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部