The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.
The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.
基金
Project supported by the National Natural Science Foundation of China （Grant No 60307004） and the Science and Technology Program of Guangzhou, Guangdong province, China （Grant No 2004Z2-D0131）.