摘要
Un-hydrogenated Diamond-like Carbon (DLC) films were prepared by pulsed laser deposition technique at different substrate temperature.The Raman spectra,the absorption and the photoluminescence spectra were measured.The dependence of structure and photoluminescence properties on deposition temperature were studied in detail.The experimental results indicate that the sp^2 sites form small clusters that consist of both olefinic chains and aromatic ring groups within the sp^3 matrix.With raising deposition temperature,the optical band gaps increase from 1.87 to 2.85 eV.The main band of photoluminescence centered at around 700nm shifts to short wavelength,and the intensity of this band increases.The photoluminescence can be attributed to carrier localization within an increasing sp^2 clusters.It was clarified that the DLC films are ordered with increasing deposition temperature.
Un-hydrogenated Diamond-like Carbon （DLC） films were prepared by pulsed laser deposition technique at different substrate temperature. The Raman spectra, the absorption and the photoluminescence spectra were measured. The dependence of structure and phetoluminescence properties on deposition temperature were studied in detail. The experimental results indicate that the sp^2 sites form small clus ters that consist of both olefinic chains and aromatic ring groups within the sp^3 matrix. With raising deposition temperature,the optical band gaps increase from 1.87 to 2.85 eV. The main band of photoluminescence centered at around 700nm shifts to short wavelength, and the intensity of this band increases. The photoluminescence can be attributed to carrier localization within an increasing sp^2 clusters. It was clarified that the DLC films are ordered with increasing deposition temperature.