摘要
Fritless packed silica gel columns were prepared using sol-gel technology, The part of a 75 μm i.d. capillary was filled with a mixture of methacryloxypropyltrimethoxysilane, toluene and hydrochloric acid. Four different photoinitiators such as benzoin methyl ether, Irgacure 819, Irgacure 1700 and Irgacure 1800 were added in the presence or absence of sodium dodecyl sulfate during the polymerization process. The above eight solutions were irradiated at 365 nm about 5-10 min to prepare the porous monolithic sol-gel columns by a one-step process.
Fritless packed silica gel columns were prepared using sol-gel technology, The part of a 75 μm i.d. capillary was filled with a mixture of methacryloxypropyltrimethoxysilane, toluene and hydrochloric acid. Four different photoinitiators such as benzoin methyl ether, Irgacure 819, Irgacure 1700 and Irgacure 1800 were added in the presence or absence of sodium dodecyl sulfate during the polymerization process. The above eight solutions were irradiated at 365 nm about 5-10 min to prepare the porous monolithic sol-gel columns by a one-step process.