摘要
The damage which represents the alternation of internal slate of material was introduced to concrete strength theory according to the theory of mechanics of continuous medium and the failure criterion of deteriorated concrete was diseussions. In the tests, ultrasonic velocity is used to establish the damage variable and to establish the damage-eoupled failure criterion of concrete under freeze-thaw. The results show that the failure surface is gradually shrinking with the increase of freeze-thaw times. Furthermore, by the comparison between the theoretical data and the testing data from the literature, the rationality of strength theory proposed in the paper acquire confirmation. The damage-coupled failure criterion presented here can indicate the influence of damage evolution on the failure surface of concrete.
The damage which represents the alternation of internal slate of material was introduced to concrete strength theory according to the theory of mechanics of continuous medium and the failure criterion of deteriorated concrete was diseussions. In the tests, ultrasonic velocity is used to establish the damage variable and to establish the damage-eoupled failure criterion of concrete under freeze-thaw. The results show that the failure surface is gradually shrinking with the increase of freeze-thaw times. Furthermore, by the comparison between the theoretical data and the testing data from the literature, the rationality of strength theory proposed in the paper acquire confirmation. The damage-coupled failure criterion presented here can indicate the influence of damage evolution on the failure surface of concrete.
基金
Supported by the National Natural Science Foun-dation of China (50578068)