使用光学金相显微镜,衍射仪及显微硬度计,研究了以Mn代替Ni后低碳高合金钢组织与性能的变化。结果表明,以Mn代Ni的低碳高合金钢在淬火回火态下可以获得与原加镍钢相同的板条马氏体组织,但其硬度比原加镍钢要高5～6HRC,而冲击韧性降低约10J·cm-2,耐蚀性只是略有下降。因此以Mn代Ni来制取低成本的低碳高合金钢具有一定的可行性。
The research was carried out using the metallographic microscope, the diffraction instrument and the microhardness tester. The variations of the structures and property of the low carbon high alloy steel, in which nickel was substituted with the isometric manganese were discussed. The results show that the low carbon high alloy steel of substituting the nickel with the manganesc could gain the same lath martensite structure as the original steel containing the nickel in the state of the double treating, however, its hardness was 5-6 HRC higher than the original nickel steel, while the impact toughness descended about 10 J·cm^-2, and the erosion resistance fell down in small amplitude, so substituting the nickel with the manganese to manufacture the low carbon high alloy steel of low cost is somewhat feasible.
出处
《兵器材料科学与工程》
CAS
CSCD
北大核心
2006年第3期25-28,共4页
Ordnance Material Science and Engineering
基金
教育部博士点基金(20040359004)
教育部重点项目(01104)
关键词
低碳高合金钢
以锰代镍
组织
性能
low carbon high alloy steel
substitute nickel with manganese
structure
property