聚苯乙烯溶胀聚苯乙烯－聚丁二烯－聚苯乙烯三嵌段共聚物微区的研究

Swelling of Styrene-Butadiene-Styrene Triblock Copolymer Microdomains with Homopolystyrene

聚苯乙烯溶胀聚苯乙烯－聚丁二烯－聚苯乙烯三嵌段共聚物微区的研究景蛟凯，谢瑞，刘春梅，姜炳政（中国科学院长春应用化学研究所高分子物理开放实验室长春１３００２２）关键词嵌段共聚物，溶胀，共混，小角Ｘ射线散射嵌段共聚物／均聚物共混体系，各嵌段会形成各自的相...

Microdomain morphology in styrene-butadiene-styrene triblock copolymer (SBS) and polystyrene (PS) blends was investigated by small angle X-ray scattering. The homopolystyrenes having molecular weight of 500 and 12000,respectively, were blended with SBS up to a concentration of 25%.As the homopolymer concentration increased,the size of the PS microdomains increased.The size of polybutadiene (PB)microdomains,on the other hand,decreased if the added polystyrene was with low molecular weight and increased if the molecular weight of the added polystyrene was large. In the blends containing low molecular weight PS, the area per junction increased with the addition of PS, while it kept almost constant for the blends containing high molecular weight PS. In the fixed PS concentration,increasing the homopolymer molecular weight increased the size of PS and PB microdomains and decreased the area per junction. The swelling in the PS microdomains became dramatically asymmetric with an increase in the homopolymer concentration and/or the homopolymer molecular weight.Over the cylinder-lamellar transition induced by the addition of thepolystyrene,the lateral expansion increased dramatically.