摘要
选择制备了系列Eu2+,Dy3+共掺杂的硼铝酸锶长余辉发光玻璃。利用发光光谱、余辉衰减曲线、热释光谱系统研究了稀土离子掺杂对长余辉玻璃发光性能的影响。研究结果表明,不同掺量组合的Eu2+及Dy3+对长余辉玻璃发光性能有不同影响,在Eu2+及Dy3+掺量比为1∶1(摩尔比)的情形下,随Eu2+离子掺量的增多,发光性能下降;在Eu2+及Dy3+掺量比为1∶2的情形下,随Eu2+离子掺量的增多,发光性能增强。在此实验基础上,围绕缺陷形态及其与稀土离子间的能量传递,提出了可能的长余辉机制。
The series of glasses co-doped with Eu^2+ and Dy^3+ were prepared. The luminescent properties were investigated by means of emission spectra, phosphorescence decay curve and thermal luminescence spectra. The results show that different Eu^2+and Dy^3+ mixing compositions exert different influences on the luminescent properties. When the mixing ratio of Eu^2+ and Dy^3+ is 1:1 (mole ratio), the luminescent proper-ties decrease with the increase of Eu^2+ content. When the Eu^2+ and Dy^3+ mixing ratio is 1 : 2 (mole ratio), the luminescent properties increase with the increase of Eu^2+ content. On the basis of the experiment re suits, around the defects formation transfer between their and rare earths ble mechanisms were discussed. and the energy ions, the possible mechanisms were discussed.
出处
《稀有金属》
EI
CAS
CSCD
北大核心
2006年第3期329-332,共4页
Chinese Journal of Rare Metals
基金
国家自然科学基金资助项目(50472077)
广东省自然科学基金重点资助项目(36706)
关键词
长余辉
发光玻璃
稀土离子
long-lasting phosphorescence
luminescent glass
rare earths ions