摘要
Polysulfonamide(PSA)was synthesized at room temperature,the polymerization based on terephthaloyl chloride and 3,3’-diaminodiphenylsulfone in the common solvent N,N-Dimethyl-acetamide(DMAc).Polysulfonamide/titanium oxide nanocomposites were prepared by sol-gel method.Tetrabutyl titanate(TBT)was added into the polysulfonamide solution,at the same time,some water was mixed to make the TBT hydrolyze.In the process,hydrochloric acid was used to catalyze the reaction.The polysulfonamide chemistry structure was characterized by FT-IR spectrum.Atomic force microscopy(AFM)was employed to observe the microstructure of the composite film.The thermal property was investigated by TGA.The results show that we have succeeded to synthesize the polysulfonamide,TiO2 particles were well distributed in the composite film and average size was about 20 nm on average,the heat-resistance of nanocomposite was batter than the pure polysulfonamide.
Polysulfonamide （PSA ） was synthesized at room temperature, the polymerization based on terephthaloyl chloride and 3,3＇-diaminodiphenylsulfone in the common solvent N,N -Dimethyl-acetamide （DMAc）. Polysulfonamide/titanium oxide nanocomposites were prepared by sol-gel method. Tetrabutyl titanate（TBT） was added into the polysulfonamide solution, at the same time ,some water was mixed to make the TBT hydrolyze. In the process, hydrochloric acid was used to catalyze the reaction. The polysulfonamide chemistry structure was characterized by FT-IR spectrum. Atomic force microscopy （AFM） was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA.
The results show that we have succeeded to synthesize the polysulfonamide, TiO2particles were well distributed in the composite film and average size was about 20 nm on average, the heat-resistance of nanocomposite was batter than the pure polysulfonamide.