Controlled radical photopolymerization of n-butyl methacrylate（n-BMA） mediated by 4-hydroxy-2,2,6,6-tetramethyl-1-piperidinyloxy（HTEMPO） was carried out in bulk at ambient temperature. It was found that obtained n-BMA homopolymers exhibited narrow polydispersities of around 1.4, which was characterized by GPC. Plots of number-average molecular weight vs. conversion and Ln（[Mo]/[M]） vs. time were liner respectively, indicating that was a controlled photopolymerization.
Controlled radical photopolymerization of n-butyl methacrylate（n-BMA） mediated by 4-hydroxy-2,2,6,6-tetramethyl-1-piperidinyloxy（HTEMPO） was carried out in bulk at ambient temperature. It was found that obtained n-BMA homopolymers exhibited narrow polydispersities of around 1.4, which was characterized by GPC. Plots of number-average molecular weight vs. conversion and Ln（[Mo]/[M]） vs. time were liner respectively, indicating that was a controlled photopolymerization.
基金
Financially supports from the National Natural Science Foundation of China(No.20274023 and 20474036)
Guangdong Province Natural Science Foundation(No.021241)are gratefully acknowledged.