聚酰胺-胺型模板法介孔氧化铝制备及性能研究(英文) 被引量：1

Synthesis and properties of mesoporous alumina with poly-amidoamine dendrimer as template

下载PDF

导出

摘要采用异丙醇铝为铝源，3．5代PAMAM为模板剂，通过油滴球过程合成了介孔γ-Al2O3微球。研究发现在所合成的氧化铝中，介孔相呈海绵状或蠕虫状随机分布的三维网络结构；其孔径主要分布在2～6nm之间，且合成的介孔氧化铝的比表面积可达340m^2／g以上。 Mesoporous spherical γ-alumina granules were prepared by an oil-drop process from aluminum isopropoxide with 3.5G PAMAM dendrimer as template. It was found that a sponge- or worm-like randomly three-dimensionally connected mesoporous network could be obtained. Its mean pore diameters vary between 2 and 6nm and its specific surface areas reached to above 340m^2/g.

作者张波王晶

机构地区东北大学冶金物理化学系大连交通大学材料与工程学院

出处《功能材料》 EI CAS CSCD 北大核心 2006年第7期1138-1141,共4页 Journal of Functional Materials

关键词介孔氧化铝溶胶-凝胶树状高分子纳米材料 mesoporous alumina sol-gel dendrimer nanomaterial

分类号 TB321 [一般工业技术—材料科学与工程]

引文网络
相关文献

参考文献11

1Firouzi A, Kumar D, Bull L M,et al. [J]. Science,1995, 267:1138-1143.
2Bagshaw S A, Prouzet E, Pinnavaia T J. [J]. Science,1995, 269:1242-1244.
3Bagshaw S A, Pinnavaia T J. [J]. Chem Int Ed Engl,1996,35: 1102-1105.
4Yada M, Kitamura H, Machida M,et al. [J]. Langmuir,1997, 13:5252-5257.
5Yada M, Hiyoshi H, Ohe K,et al. [J]. Inorg Chem,1997, 36: 5565-5569.
6Liu Xinghua,Wei Yen,Jin Danliang,et al. [J]. Materials Letters,2000, 42: 143-149.
7Lee A T, Tech B. Molecular Modeling Studies of Dendrimers and Hyperbranched Polymers [M]. USA: Indian Institute of Technology, 1996.
8Buelna G, Lin Y S. [J]. Microporous and Mesoporous Materials,2001, 42: 67-76.
9Wang Zhongmin, Lin Y S. [J]. Journal of Catalysis,1998, 174: 43-51.
10Gonzalez-Pena V, Diaz I,Marquez-Alvarez C,et al. [J]. Microporous and Mesoporous Materials,2001, 44-45 : 203-210.

同被引文献28

1李瑞勇,李晓杰,赵峥,谢兴华,曲颜东,王占磊,陈涛.爆轰合成纳米γ—氧化铝粉体的实验研究[J].材料与冶金学报,2005,4(1):27-29. 被引量：10
2陈胜福,黄坚,李建文.多品种氧化铝开发进展、动向及市场现状[J].材料导报,2006,20(7):22-26. 被引量：15
3张李锋,石悠,赵斌元,胡克鳌,唐建国.γ-Al_2O_3载体研究进展[J].材料导报,2007,21(2):67-71. 被引量：41
4张波,王晶.不同模板剂对介孔氧化铝孔径调节作用[J].功能材料与器件学报,2007,13(2):150-154. 被引量：7
5李国印,支建平,张玉林.表面活性剂对活性氧化铝孔结构的影响[J].日用化学工业,2007,37(3):156-159. 被引量：2
6Bagshaw S A,Pinnavaia TJ. Mesoporous alumina molecular sieves[J]. Angew Chem Int Ed, 1996, 35(10) : 1102.
7Yang P, Zhao D, Margolese D I, et al. Block copolymer ternplating synthesis of rnesoporous metal oxides with large ordering lengths and sernicrystalline framework[J]. Chem Mater, 1999,11 : 2813.
8Aguado J, Escola J M, Castro M C,et al. Sol-gel synthesis of mesostructured "/-alumina templated by cationic surfactants[J]. Microp Mesop Mater, 2005,83 : 181.
9Park Hoseok, Seong Ho Yang, Jun Young-Si, et al. Facile route to synthesize large-mesoporous γ-alumina by room temperature ionic liquids[J]. Chem Mater, 2007,19(3) :535.
10Liu Qian, Wang Aiqin, Wang Xuehai, et al. Synthesis, characterization and catalytic applications of mesoporous γ-alumina from boehmite sol [J]. Microp Mesop Mater, 2008, 111:323.

引证文献1

1王俊娥,周秋生,刘桂华.高比表面积γ-Al_2O_3的制备研究进展[J].材料导报,2010,24(15):52-55. 被引量：3

二级引证文献3

1周仁美,喻琴,王树元,金凌云,胡庚申,罗孟飞.La_2O_3的添加方式对Al_2O_3热稳定性的影响[J].工业催化,2012,20(11):25-29.
2胡小夫,张敏,李国良,殷长龙,崔瑞利,赵瑞玉,刘晨光.γ-Al2O3载体的固相法合成及Ni-Mo-P/γ-Al2O3催化剂的加氢脱硫性能[J].石油学报（石油加工）,2013,29(2):191-197. 被引量：3
3张晓阳,朱玲,朱玲玲,孟令硕.介孔氧化铝制备及对正丁烷吸附性能的研究[J].材料导报,2013,27(10):99-103. 被引量：2

1赵和.750ml勃根第酒瓶初型模设计探讨[J].中国包装,1995,15(4):61-61. 被引量：2
2付银萍,郭秀生,于德梅.树状高分子材料的应用研究进展[J].化工新型材料,2011,39(S1):22-26. 被引量：1
3张波,王晶,刘艳霞,高宏.不同代数PAMAM树状高分子材料的热重分析[J].有色矿冶,2005,21(S1):64-65. 被引量：1
4拜耳材料科学公司推出新型模内涂装法[J].工程塑料应用,2006,34(7):65-65.
5吴志锋,陈刚,赵玉涛,张勇.凝固速率对Al_3Ti/Al复合材料显微组织的影响[J].热加工工艺,2011,40(18):92-94. 被引量：1
6陈凯,俞蒙槐,胡上序,于思荣,何镇明.ZA22/Al_2O_(3f) 复合材料力学性能的神经网络模拟研究[J].材料工程,1997,25(10):14-16.
7全洪杰,郝建广.模组背板定位柱的包装技术研究[J].广东科技,2015,24(24):66-67.
8张连华.钨极氩弧焊在微型膜动式压力控制器上的应用[J].机车车辆工艺,1997(3):26-29.
9武宏,牛立斌,许云华.区域式无压熔渗制备复合材料的研究[J].铸造技术,2008,29(10):1402-1405.
10治明.仪表板用新型TPU材料[J].国外塑料,2009,27(5):95-95.

功能材料

2006年第7期

浏览历史

内容加载中请稍等...

聚酰胺-胺型模板法介孔氧化铝制备及性能研究(英文) 被引量：1

参考文献11

同被引文献28

引证文献1

二级引证文献3

相关作者

相关机构

相关主题

浏览历史