摘要
Electroless Co-Fe-P alloys were deposited from an alkaline bath, containing boric acid as a buffer agent and sodium citrate as a complexing agent. As a result, with the increase of pH of the bath, the iron content of the deposit increased, whereas the cobalt and phosphorus contents decreased. The structure of the deposit was investigated using X-ray diffraction （XRD） and transmission electron microscope （TEM）. The deposit consisted of hexahedron phase Co, cubic phase Fe-Co, and amorphous phase （crystalline）. The magnetic performances of the deposit were studied using vibrating sample magnetometer （VSM）. The more the content of Fe and the less the content of P （the content of Co being less）, the better the magnetic performances of the deposit. The Co-Fe-P deposit was suitable for use as soft magnetic material.
Electroless Co-Fe-P alloys were deposited from an alkaline bath, containing boric acid as a buffer agent and sodium citrate as a complexing agent. As a result, with the increase of pH of the bath, the iron content of the deposit increased, whereas the cobalt and phosphorus contents decreased. The structure of the deposit was investigated using X-ray diffraction （XRD） and transmission electron microscope （TEM）. The deposit consisted of hexahedron phase Co, cubic phase Fe-Co, and amorphous phase （crystalline）. The magnetic performances of the deposit were studied using vibrating sample magnetometer （VSM）. The more the content of Fe and the less the content of P （the content of Co being less）, the better the magnetic performances of the deposit. The Co-Fe-P deposit was suitable for use as soft magnetic material.
基金
Acknowledgements-This work was supported by the Fujian Provincial Natural Science Foundation of China （No. E0210020）.