研究了碳含量（8．39％～14．20％）和TiO2（0．35％）对主要成分（％）为21．98-27．93CaO．32.03～43·20SiO2，4．58～5．83Al2O3保护渣在1120～1200℃时流动性的影响。结果表明，液态保护渣有剩余碳以及含钛钢中的Ti氧化生成TiO2进入保护渣后均会恶化保护渣的流动性能。
The effect of C content （8.39% - 14.20% ） and TiO2 （0. 35% ） on fluidity of mold flux - 21.98 - 27.93 CaO, 32. 03 -43.20 SiO2, 4. 58 -5. 83 Al2O3 at 1 120- 1 200 ℃ has been studied. The results showed that residual carbon in flux and TiO2 in flux which was produced by Ti oxidation in Ti bearing steel led to worse fluidity of mold flux.