摘要
从理论和实践两方面阐述钼对0Cr15Ni5Cu2Ti钢固溶强度的影响,总结出提高钼含量是解决0Cr15Ni5Cu2Ti钢固溶强度偏低的有效方法。试验结果表明,残钼在0．20%～0．25%之间提高该钢固溶强度作用明显。
Effect of Molybdenum on solid solution strength of steel OCr15Ni5Cu2Ti was expounded from two aspects of theory and practice , it is obtained that increasing content of Molybdenum is the effective approach to solve the problem of lower solution strength of steel OCr15NiSCu2Ti . The test result showed that solid solution strength could be obviously increased when residual molybdenum was between 0.20% and 0.25%
出处
《特钢技术》
CAS
2006年第2期29-31,共3页
Special Steel Technology