摘要
The Ti-Al ohmic contact to n-type 6H-SiC has been fabricated. An array of TLM （transfer length method） test patterns with Au/Ti/A1/Ti/SiC structure is formed on N-wells created by P^＋ ion implantation into Si-faced p-type 6H-SiC epilayer. The specific contact resistance pc as low as 8.64×10-6Ω·cm^2 is achieved after annealing in N2 at 900℃ for 5min. The sheet resistance Rsh of the implanted layers is 975Ω. X-ray diffraction （XRD） analysis shows the formation of Ti3SiC2 at the metal/n-SiC interface after thermal annealing, which is responsible for the low resistance contact.
The Ti-Al ohmic contact to n-type 6H-SiC has been fabricated. An array of TLM （transfer length method） test patterns with Au/Ti/A1/Ti/SiC structure is formed on N-wells created by P^＋ ion implantation into Si-faced p-type 6H-SiC epilayer. The specific contact resistance pc as low as 8.64×10-6Ω·cm^2 is achieved after annealing in N2 at 900℃ for 5min. The sheet resistance Rsh of the implanted layers is 975Ω. X-ray diffraction （XRD） analysis shows the formation of Ti3SiC2 at the metal/n-SiC interface after thermal annealing, which is responsible for the low resistance contact.
基金
Project supported by the National Basic Research Program of China （Grant No 2002CB311904）, the National Defense Basic Research Program of China （Grant No 51327010101） and the National Natural Science Foundation of China （Grant No 60376001）.