The effect of fly ash on controlling alkail-silica rection （ASR） in simudated alkali solution was studied. The expausion of mortar bars and the content of Ca（ OH）2 in cement paste cured at 80 °G for 91 d were measured. Traasmission electron microscopy （TEM） and high-resolution transmission electron microscot9 （HRTEM） were employed to study the microstructure of C-S-H. TEM/ energy dispersive spectroscopy （EDS） leas then used to determine the composition of C-S-H. The pore structure of the paste was analyzed by mercury intntsion porosimetry （MIP）. The results show that the contents of fly ash of 30% and 45% can well inhibit ASR. And the content of Ca（OH） 2 decreases with the increase of fly ash. That fly ash reacted with Ca（OH）2 to produce C-S-H with a low Ca/Si molar ratio could bind more Na^＋ and K^＋ ious, and produce a reduction in the amount of soluble alkali available for ASR. At the same time, the C- S- H produced by pozzolanic reaction converted large pores to snudler ones （ gel pores smaller than 10 nm ） to deusify the pore structure. Perhaps that could inhibit alkali trausport to aggregate for ASR.
The effect of fly ash on controlling alkail-silica rection （ASR） in simudated alkali solution was studied. The expausion of mortar bars and the content of Ca（ OH）2 in cement paste cured at 80 °G for 91 d were measured. Traasmission electron microscopy （TEM） and high-resolution transmission electron microscot9 （HRTEM） were employed to study the microstructure of C-S-H. TEM/ energy dispersive spectroscopy （EDS） leas then used to determine the composition of C-S-H. The pore structure of the paste was analyzed by mercury intntsion porosimetry （MIP）. The results show that the contents of fly ash of 30% and 45% can well inhibit ASR. And the content of Ca（OH） 2 decreases with the increase of fly ash. That fly ash reacted with Ca（OH）2 to produce C-S-H with a low Ca/Si molar ratio could bind more Na^＋ and K^＋ ious, and produce a reduction in the amount of soluble alkali available for ASR. At the same time, the C- S- H produced by pozzolanic reaction converted large pores to snudler ones （ gel pores smaller than 10 nm ） to deusify the pore structure. Perhaps that could inhibit alkali trausport to aggregate for ASR.
基金
Founded bythe National Basic Research Programof China"973"(No.2001CB610706)