稠油热采注蒸汽管道爆裂原因分析及对策

Analysis and Countermeasures for Pipe Cracking During Steam Injection

针对胜利油田稠油热采注蒸汽管道运行参数高，起停频繁，腐蚀严重，爆裂突然等特点，详细分析了稠油热采注蒸汽管道爆裂原因，主要是由高氧化与腐蚀，氢脆腐蚀造成注蒸汽管道爆裂，针对稠油热采注蒸汽管道爆裂原因。

To tackle the problems with steam injection pipe,such as high operating parameters, frequent starts and stops,serious corrosion and bursting,this paper details the reasons for pipe cracking due to high Oxidation and corrosion and hydrogen embrittlement corrosion and puts forward reasonable countermeasures.