A novel, reactive amide-bridged ladder polyvinylsiloxane （abbr. LP） with Mn= 2.4×10^4 was synthesized for the first time by means of aryl amide H-bonding self-assembled template. The regularity of LP was characterized by the XRD, ^29Si NMR and DSC methods. XRD analysis demonstrated the ladder width w = 9.09A and the ladder thickness t = 3.89A, respectively, which are approximately consistent with the molecular simulation-calculated ones： w＇= 10.60A and t＇= 3.06A. ^29Si NMR displayed a resonance peak with small half peak width, △1/2 - 4 ppm, for the moiety [=Si（Vi）O2/2-]n of LP. Besides, as a collateral evidence, DSC measurement revealed a high glass transition temperature Tg = 225℃, suggesting high stiffness of the ladder main chain of LP.
A novel, reactive amide-bridged ladder polyvinylsiloxane （abbr. LP） with Mn= 2.4×10^4 was synthesized for the first time by means of aryl amide H-bonding self-assembled template. The regularity of LP was characterized by the XRD, ^29Si NMR and DSC methods. XRD analysis demonstrated the ladder width w = 9.09A and the ladder thickness t = 3.89A, respectively, which are approximately consistent with the molecular simulation-calculated ones： w＇= 10.60A and t＇= 3.06A. ^29Si NMR displayed a resonance peak with small half peak width, △1/2 - 4 ppm, for the moiety [=Si（Vi）O2/2-]n of LP. Besides, as a collateral evidence, DSC measurement revealed a high glass transition temperature Tg = 225℃, suggesting high stiffness of the ladder main chain of LP.