摘要
A new type additive was added to the non-self-fluxing copper powdered alloy, and the powder showed satisfactory performance of spraying and fusing, self-protecting, and self-fluxing in the oxygen-acetylene flame spraying and fusing process. The additive was melted and could absorb copper oxide when spraying, then it created a layer of film to cover the copper liquid, which protected the copper liquid from oxidizing efficiently and promoted it wetting on iron surface. Thus it lead to real diffusion between Cu and Fe, which resolved the diffwulty of combining Cu with Fe and reduced the limitation of the powder, and it promoted the usage value of general powder. Through analysis of microstructures, it was found that the fastness and compactness of the combining interface was excellent as well as the diffusing of transition area, and the hardness was suitable, which meant that the performance could meet the needs of high quality valves completely.
A new type additive was added to the non-self-fluxing copper powdered alloy, and the powder showed satisfactory performance of spraying and fusing, self-protecting, and self-fluxing in the oxygen-acetylene flame spraying and fusing process. The additive was melted and could absorb copper oxide when spraying, then it created a layer of film to cover the copper liquid, which protected the copper liquid from oxidizing efficiently and promoted it wetting on iron surface. Thus it lead to real diffusion between Cu and Fe, which resolved the diffwulty of combining Cu with Fe and reduced the limitation of the powder, and it promoted the usage value of general powder. Through analysis of microstructures, it was found that the fastness and compactness of the combining interface was excellent as well as the diffusing of transition area, and the hardness was suitable, which meant that the performance could meet the needs of high quality valves completely.