The preparation of nanometer γ-Fe2O3 through an electrochemical process was studied at room temperature, using a metal iron plate as sacrificing anode and a sheet of stainless steel as cathode, in non-aqueous mediate containing （Bu）4 NBr as support electrolyre and 2% （vol%） water. The powdery particles obtained were then calcined at 300 ℃. The products were characterized by IR, XRD, SEM, TEM and laser particle size analyser, indicating the fine particle is a pure nanometer γ-Fe2O3. The morphology is like coneshaped and their average size is 22.0 nm. Furthermore the VSM spectrum shows that the particle＇s coercivity （3.9 × 10^3 A/m） is rather small, presenting the excellent super-paramagnetism.
The preparation of nanometer γ-Fe2O3 through an electrochemical process was studied at room temperature, using a metal iron plate as sacrificing anode and a sheet of stainless steel as cathode, in non-aqueous mediate containing （Bu）4 NBr as support electrolyre and 2% （vol%） water. The powdery particles obtained were then calcined at 300 ℃. The products were characterized by IR, XRD, SEM, TEM and laser particle size analyser, indicating the fine particle is a pure nanometer γ-Fe2O3. The morphology is like coneshaped and their average size is 22.0 nm. Furthermore the VSM spectrum shows that the particle＇s coercivity （3.9 × 10^3 A/m） is rather small, presenting the excellent super-paramagnetism.