Broadband near-infrared emission from transparent Ni^2＋-doped sodium aluminosilicate glass-ceramics is observed. The broad emission is centred at 1290nm and covers the whole telecommunication wavelength region （1100- 1700hm） with full width at half maximum of about 340hm. The observed infrared emission could be attributed to the 3T2（F） → 3A2（F） transition of octahedral Ni^2＋ ions that occupy high-field sites in nanocrystals. The product of the lifetime and the stimulated emission cross section is 2.15 × 10^-24 cm^2s. It is suggested that Ni^2＋- doped sodium aluminosilicate glass ceramics have potential applications in tunable broadband light sources and broadband amplifiers.
Broadband near-infrared emission from transparent Ni^2＋-doped sodium aluminosilicate glass-ceramics is observed. The broad emission is centred at 1290nm and covers the whole telecommunication wavelength region （1100- 1700hm） with full width at half maximum of about 340hm. The observed infrared emission could be attributed to the 3T2（F） → 3A2（F） transition of octahedral Ni^2＋ ions that occupy high-field sites in nanocrystals. The product of the lifetime and the stimulated emission cross section is 2.15 × 10^-24 cm^2s. It is suggested that Ni^2＋- doped sodium aluminosilicate glass ceramics have potential applications in tunable broadband light sources and broadband amplifiers.
基金
Support by the Postdoctoral Science Foundation of China under Grant No 2005038020.